旭硝子AK-225AES清洗剂


ASAHIKLIN AK-225AES

 

INTRODUCTION

ASAHIKLIN AK-225AES was developed as a defluxing agent. AK-225AES is an azeotrope-like mixture of AK-225, ethanol and stabilizer andis suitable for use in a vapor degreaser. It effectively removes flux residues as well as ionic soils from printed circuit boards and other electronic devices.  AK-225AES is 95% VOC free as of the October 8, 1996 Federal Register.

 

PHYSICAL PROPERTIES

Physical properties of AK-225AES are shown in Table 1.




Table 1  Physical Properties of AK-225AES.



 


 
  AK-225AES CFC-113AES(1)
Boiling Point ( C) 52 46.5
Freezing Point ( C) -138 -41.8
Density (g/cm3) 1.49 1.50
Viscosity (cP, 25 C) 0.61 0.66
Surface Tension (dyne/cm, 25 C) 16.8 18.5(2)
Vapor Pressure (mmHg, 25 C) 291 360
Latent Heat of Vaporization (cal/g, b.p.) 40.6 42.9
Relative Evaporation Rate (Ether=100) 81 120
Specific Heat (cal/g   C) 0.27 0.272(2)
Solubility of Water (wt%, 25 C) 0.33 0.25
Solubility in Water (wt%, 25 C) 0.053  
Flash Point ( C) None None
KB Value 41 39



(1CFC-113AES is a mixture of CFC-113, alcohol and stabilizer.     (2At 20 C.



 



 



CLEANING PROCEDURES



It is recommended that AK-225AES be used in a vapor degreaser for maximum cleaning efficiency,



economy and emission control. Cleaning procedures for AK-225AES are quite similar to those of CFC-



113AES (a mixture of CFC-113, ethanol and stabilizer). The procedures consist of immersing a workload into the boiling solvent, rinsing orspraying with cool solvent and drying in solvent vapor.



 



 



MATERIAL COMPATIBILITY



AK-225AES is compatible with many common materials under typical cleaning conditions. However,



certain plastics and elastomers are affected by AK-225AES. It is recommended that material compatibility be tested prior to use.



 



Tables 2 and 3 show the effect of AK-225AES on unstressed plastics under typical cleaning conditions (at the boiling point for fiveminutes) and also under extreme conditions (3 days at the boiling point). AK-



225AES is compatible with most plastics except polymethyl methacrylate. Some plastics such as polycarbonate, ABS resins andpolyphenylene oxide, however, will crack or craze if they are stressed.



 



Table 2  Effect of AK-225AES on Unstressed Plastics for 5 minutes at the Boiling Point.
 
  AK-225AES CFC-113AES
  Weight
Change(%)
LinearSwell
(%)
Extractables
(%)
Weight
Change(%)
LinearSwell
(%)
Extractables
(%)
Polyvinyl chloride (rigid) <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
Polyvinyl chloride (plasticized) 2.1 0.4 0.7 <0.1 <0.1 0.3
Polyethylene (HP) 0.1 0.2 <0.1 0.2 <0.1 <0.1
Polyethylene (LP) 0.4 0.5 0.1 <0.1 <0.1 0.1
Polypropylene 0.1 0.5 0.1 <0.1 <0.1 <0.1
Polystyrene 0.8 0.3 <0.1 0.5 <0.1 0.1
Polymethyl methacrylate (Acrylic) crack crack crack <0.1 <0.1 <0.1
Polycarbonate <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
Polyacetal <0.1 <0.1 0.1 <0.1 <0.1 <0.1
Polyphenylene oxide 0.1 0.2 0.1 <0.1 <0.1 <0.1
Phenolic <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
ABS 1.1 0.1 0.1 <0.1 <0.1 <0.1
Nylon 6 <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
Nylon 66 <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
Polyester (FR) <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
PTFE <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
PCTRE <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
Epoxy (FR) <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
Polyphenylene sulfide <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
Polybutylene terephthalate <0.1 <0.1 <0.1 <0.1 <0.1 <0.1

 

 

Table 3  Effect of AK-225 AES on Unstressed Plastics for 3 Days at the Boiling Point.
 
  AK-225 AES CFC-113 AES
  Weight
Change(%)
LinearSwell
(%)
Extractables
(%)
Weight
Change(%)
LinearSwell
(%)
Extractables
(%)
Polyvinyl chloride (rigid) <0.1 <0.1 0.2 <0.1 <0.1 0.2
Polyvinyl chloride (plasticized) Stiffen & Deform 19.9 2.2 49.3
Polyethylene (HP) 3.2 0.7 <0.1 8.3 1.2 0.3
Polyethylene (LP) 8.0 1.5 0.1 7.2 1.1 0.3
Polypropylene 10.0 1.9 0.2 17.4 2.9 0.4
Polystyrene 28.6 0.8 0.9 42.5 3.0 2.8
Polymethyl methacrylate (Acrylic) Dissolve Dissolve Dissolve 30.2 1.5 0.3
Polycarbonate 7.7 0.4 <0.1 0.6 0.5 0.3
Polyacetal 1.2 0.3 0.2 1.0 0.2 0.2
Polyphenylene oxide 13.8 0.6 1.9 30.8 0.8 1.0
Phenolic -0.6 <0.1 <0.1 -0.2 <0.1 0.5
ABS 73.4 1.4 0.7 1.2 0.2 1.2
Nylon 6 0.1 0.2 <0.1 -0.3 0.2 0.3
Nylon 66 <0.1 <0.1 <0.1 0.6 0.1 0.5
Polyester (FR) 3.0 <0.1 0.2 1.0 0.1 0.1
PTFE 2.2 0.5 0.2 1.0 0.1 0.1
PCTRE 2.8 0.4 <0.1 1.6 0.2 0.2
Epoxy (FR) <0.1 <0.1 <0.1 0.2 <0.1 0.1
Polyphenylene sulfide <0.1 <0.1 <0.1 <0.1 <0.1 <0.1
Polybutylene terephthalate 0.4 0.2 <0.1 0.5 <0.1 <0.1


Tables 4 and 5 show the effect of AK-225 AES on elastomers under normal cleaning conditions (5 minutes at the boiling point) and also underextreme conditions (3 days at the boiling point). AK-225 AES affects some elastomers differently than CFC-113. Gaskets and/or seals used incleaning equipment should be made of polytetrafluoroethylene, EPDM or chloroprene. Mechanical pump seals in solvent re-circulationpumps should be polytetrafluoroethylene. Seal-less pumps are ideal.

 

 

Table 4.  Effect of AK-225 AES on Elastomers for 5 Minutes at the Boiling Point.

 
  AK-225 AES CFC-113 AES
  Weight
Change(%)
LinearSwell
(%)
Extractables
(%)
Weight
Change(%)
LinearSwell
(%)
Extractables
(%)
Polysulfide rubber FA (T) 5.5 2.4 1.4 1.1 0.9 0.8
Natural rubber (NR) 2.9 0.9 0.8 3.6 0.6 2.6
Urethane rubber (U) 10.9 1.6 0.3 1.6 0.9 0.4
Isobutylene isoprene rubber (IIR) 2.0 0.5 1.7 5.7 0.3 3.1
Polychloroprene (CR) 2.1 0.3 0.8 1.6 <0.1 0.7
Fluoroelastomer E (FKM) 5.4 1.6 0.2 1.0 0.4 0.3
Chlorosulfonated polyethylene(CSM) 1.4 0.4 1.8 1.1 0.3 1.5
Silicone rubber (Q) 32.9 9.8 0.5 25.4 6.1 0.5
Nitryl Rubber (NBR) 11.5 2.9 1.6 1.8 1.0 1.5
Ethylene propylene dieneterpolymer
(EPDM)
2.3 -0.1 1.5 4.1 0.7 3.7

 

 

 

 

Table 5. Effect of AK-225 AES on Elastomers for 3 Days at the Boiling Point.

 
  AK-225AES CFC-113AES*
  Weight
Change(%)
LinearSwell
(%)
Extractables
(%)
Weight
Change(%)
LinearSwell
(%)
Extractables
(%)
Polysulfide rubber FA (T) 114.8 24.5 10.4 19.8 2.3 17.0
Natural rubber (NR) 26.4 7.2 4.9 30.1 7.3 23.1
Urethane rubber (U) 170.2 32.3 0.2 32.2 7.3 3.3
Isobutylene isoprene rubber (IIR) 6.6 -0.4 14.1 40.1 5.8 30.5
Polychloroprene (CR) 26.6 4.1 7.7 18.9 5.4 15.2
Fluoroelastomer E (FKM) 65.6 20.6 1.9 32.0 12.0 1.8
Chlorosulfonated polyethylene(CSM) 1.4 -2.0 17.3 8.4 1.4 24.1
Silicone rubber (Q) 201.0 31.2 2.0 111.0 40.5 5.9
Nitryl Rubber (NBR) 160.9 31.9 13.4 20.5 3.5 22.1
Ethylene propylene dieneterpolymer
(EPDM)
8.2 0.4 14.0 41.3 4.8 33.2

*CFC-113AES is a mixture of CFC-113, ethanol and stabilizer.
AK-225 AES is compatible with common metals. Table 6. Shows the effect of AK-225 AES on common metals after 7 days exposure at theboiling point.
Table 6. Effect of AK-225 AES on Metals after 7 Days at Boiling Point.
  AK-225 AES CFC-113 AES*
  Wt Change
(mg/dm2  day)
Cl
(ppm)
Corrosion WtChange
(mg/dm2  day)
Cl
(ppm)
Corrosion
Steel (SPCC-SB) N.D. N.D. N.A. N.D. N.D. N.A.
Stainless Steel (SS-304) N.D. N.D. N.A. N.D. N.D. N.A.
Magnesium N.D. N.D. N.A. N.D. N.D. N.A.
Aluminum N.D. N.D. N.A. N.D. N.D. N.A.
Zinc N.D. N.D. N.A. N.D. N.D. N.A.
Silver N.D. N.D. N.A. N.D. N.D. N.A.
Copper N.D. N.D. N.A. N.D. N.D. N.A.
Nickel Silver N.D. N.D. N.A. N.D. N.D. N.A.
Phosphorous bronze N.D. N.D. N.A. N.D. N.D. N.A.
Brass N.D. N.D. N.A. N.D. N.D. N.A.
Tin N.D. N.D. N.A. N.D. N.D. N.A.
Solder N.D. N.D. N.A. N.D. N.D. N.A.
Tin Plating N.D. N.D. N.A. N.D. N.D. N.A.
Cadmium Plating N.D. N.D. N.A. N.D. N.D. N.A.
Nickel Plating N.D. N.D. N.A. N.D. N.D. N.A.
Nickel-Chrome Plating N.D. N.D. N.A. N.D. N.D. N.A.
Aluminite N.D. N.D. N.A. N.D. N.D. N.A.
Note:  
N.D. – Not Detectable
Detection Limit of Weight Change: <0.1mg/dm2  day
   
N.A. – Not Apparent
Detection Limit of Cl Ion: <0.1ppm
Detection Method: Visual
STABILITY
Stability of AK-225AES is similar to CFC-113AES. Followings are the results of accelerated oxidation
testing. The test method is as follows*
Test Method: Solvents were refluxed for 48hrs under tungsten lamp irradiation with moisture saturated oxygen bubbled throughcontinuously. Test coupons made of carbon steel were located in both the vapor and liquid phases.
Test Results after 48hrs
Solvent Acidity as HCl (ppm) Corrosion
AK-225AES Not Detectable None Apparent
CFC-113AES Not Detectable None Apparent
Detection Limit of Acidity: <0.2ppm
CONTAMINATION LEVEL CONTROL
To maintain effective cleaning in a vapor degreaser, it is important to keep contamination levels in the boil sump below, for example, 20% byweight. The level depends on the required cleanliness.  Contamination is monitored by measuring the specific gravity and boiling point ofthe solvent. Figures 1 and 2 offer
typical specific gravity and boiling point curves which are used to determine when the boil sump should be recharged. When first utilizingAK-225AES it is recommended that the boil sump be monitored weekly to insure that it is operating within the recommended guidelines.However, workloads vary from user to user and the frequency of monitoring can be shortened or extended based upon individual needs.
As with any solvent contamination such as flux will accumulate and it is important to maintain the pH of the solvent in the water separatorabove 5.
Minimize introduction of water into equipment containing AK-225AES. Alcohol and the stabilizer in AK-225 will be extracted by large amount of water.